標題: | Microstructural Characterization and Mechanical Properties of Duplex and Super Austenitic Stainless Steels under Dynamic Impact Deformation | 作者: | Wang, Shing-Hoa Hsiao, Wuan-Yun Yang, Yo-Lun Chen, Chih-Yuan Yang, Jer-Ren Lee, Woei-Shyan Chen, Chien-Chon Chiu, Po-Kai |
關鍵字: | high-speed impact deformation;stainless steel;strain-induced martensite;transmission electron microscopy;twin | 公開日期: | 2-八月-2021 | 出版社: | SPRINGER | 來源出版物: | JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 摘要: | The microstructures of the duplex stainless steels (DSSs) SAF 2507 and SAF 2205 and the super austenitic stainless steel (SASS) 254 SMO were studied by subjecting the materials to high-speed dynamic impact tests under two strain rates: 8.5 x 10(2) and 5 x 10(3) s(-1). Regardless of the material, the mechanical properties, that is, the flow stress-strain curves, and microstructures were strongly affected by the impact loading rate. In addition, within the alpha phase, as the strain rate increased, the number of tangled dislocations in the alpha phase increased in the SAF 2507 DSS and SAF 2205 DSS. However, within the gamma phase, several persistent slip bands intersecting with twins were observed in the SAF 2205 DSS, even after deformation at the lower strain rate of 8.5 x 10(2) s(-1). Furthermore, deformation twins occurred only in the gamma phase after impact deformation at the higher strain rate of 5 x 10(3) s(-1) in both DSSs. A strain-induced martensite structure (alpha ') was observed in the 254 SMO SASS. Therefore, the mechanical properties of stainless steels are strongly associated with the deformation structures, which are influenced heavily by the deformation rate. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/17778 | ISSN: | 1059-9495 | DOI: | 10.1007/s11665-021-06063-x |
顯示於: | 機械與機電工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。