dc.description.abstract | The fatigue crack growth behaviors of AISI 316L stainless steel (SS) welds in air and gaseous hydrogen were evaluated, and further compared with the base plate. In air, the fatigue crack growth rate (FCGR) of the weld after heat-treatment at 1050 oC/1 h was similar to that of the base metal. Furthermore, all specimens became susceptible to hydrogen-accelerated crack growth. Mainly quasi-cleavage fracture related with the strain-induced martensite accounted for the accelerated crack growth in hydrogen. A smaller amount of martensite in the weld was responsible for the decreased susceptibility to hydrogen-enhanced fatigue crack growth relative to the base metal. | en_US |
dc.language.iso | en | en_US |
dc.subject | A. Stainless steel | en_US |
dc.subject | B. Hydrogen embrittlement | en_US |
dc.subject | C. Welding | en_US |
dc.title | Hydrogen-assisted fatigue crack growth of AISI 316L stainless steel weld | en_US |
dc.type | journal article | en_US |
dc.identifier.doi | 10.1016/j.corsci.2008.08.016 | - |
dc.relation.journalvolume | 50 | en_US |
dc.relation.journalissue | 11 | en_US |
dc.relation.pages | 2973-2980 | en_US |
item.grantfulltext | none | - |
item.fulltext | no fulltext | - |
item.languageiso639-1 | en | - |
item.openairetype | journal article | - |
item.openairecristype | http://purl.org/coar/resource_type/c_6501 | - |
item.cerifentitytype | Publications | - |
crisitem.author.dept | College of Electrical Engineering and Computer Science | - |
crisitem.author.dept | Department of Optoelectronics and Materials Technology | - |
crisitem.author.dept | National Taiwan Ocean University,NTOU | - |
crisitem.author.dept | Center of Excellence for Ocean Engineering | - |
crisitem.author.dept | Ocean Energy and Engineering Technology | - |
crisitem.author.orcid | 0000-0003-1644-9745 | - |
crisitem.author.parentorg | National Taiwan Ocean University,NTOU | - |
crisitem.author.parentorg | College of Electrical Engineering and Computer Science | - |
crisitem.author.parentorg | National Taiwan Ocean University,NTOU | - |
crisitem.author.parentorg | Center of Excellence for Ocean Engineering | - |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。