Mechanical and Anticorrosive Properties of TiNbTa and TiNbTaZr Films on Ti-6Al-4V Alloy

Abstract

In this study, TiNbTa and TiNbTaZr films were utilized as protective coatings on a Ti-6Al-4V alloy to inhibit corrosive attacks from NaCl aqueous solution and simulated body fluid. The structural and mechanical properties of multicomponent TiNbTa(Zr) films were investigated. The corrosion resistance of the TiNbTa(Zr)-film-modified Ti-6Al-4V alloy was evaluated using potentiodynamic polarization tests in a NaCl aqueous solution. The results indicate that the TiNbTa(Zr) films with high Ti and Zr contents exhibited inferior corrosive resistance related to the films with high Ta and Nb contents. Moreover, the TiNbTa(Zr)-coated Ti-6Al-4V plates were immersed in Ringer's solution for eight weeks; this solution was widely used as a simulated body fluid. The formation of surficial oxide layers above the TiNbTa(Zr) films was examined using transmission electron microscopy and X-ray photoelectron spectroscopy, which prevented the elution of Al and V from the Ti-6Al-4V alloy. Ti33Nb19Ta21Zr27, Ti15Nb68Ta8Zr9, and Ti8Nb8Ta79Zr5 films are suggested as preferential candidates for TiNbTa(Zr)/Ti-6Al-4V assemblies applied as biocompatible materials.