Title: | The Evolution of Cast Microstructures on the HAZ Liquation Cracking of Mar-M004 Weld | Authors: | Yi-Hsin Cheng Jyun-Ting Chen Ren-Kae Shiue Leu-Wen Tsay |
Keywords: | liquation crack;heat-affected zone;Mar-M004 superalloy;repair welding | Issue Date: | Jan-2018 | Journal Volume: | 8 | Journal Issue: | 1 | Start page/Pages: | 35 | Source: | Metals | Abstract: | The causes of liquation cracking in the heat-affected zone (HAZ) of a cast Mar-M004 superalloy weld were investigated. X-ray diffraction (XRD), electron probe microanalyzer (EPMA), and electron backscatter diffraction (EBSD) were applied to identify the final microconstituents at the solidification boundaries of the cast alloy. Fine borides and lamellar eutectics were present in front of some γ-γ′ colonies, which were expected to be liquefied prematurely during welding. The metal carbide (MC) enriched in Nb, Hf; M3B2 and M5B3 borides enriched in Cr and Mo; and lamellar Ni-Hf intermetallics were mainly responsible for the induced liquation cracking of the Mar-M004 weld, especially the MC carbides. Scanning electron microscope (SEM) fractographs showed that the fracture features of those liquation cracks were associated with the interdendritic constituents in the cast superalloy. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/4653 | ISSN: | 2075-4701 | DOI: | 10.3390/met8010035 |
Appears in Collections: | 光電與材料科技學系 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.