標題: | Effect of oxygen pressure on the oxidation behavior of NiCoCr medium-entropy alloy at 800 degrees C | 作者: | Kai, W. Lin, H. C. Cheng, F. P. Hsieh, H. H. Lin, W. T. Chen, D. Kai, J. J. |
關鍵字: | Medium-entropy alloy;SEM;TEM;Scales | 公開日期: | 1-六月-2021 | 出版社: | PERGAMON-ELSEVIER SCIENCE LTD | 卷: | 185 | 來源出版物: | CORROSION SCIENCE | 摘要: | The oxidation behavior of NiCoCr medium-entropy alloy was investigated at 800 degrees C in various oxygen pressures from 10 to 10(5) Pa. The results showed that the oxidation kinetics of NiCoCr followed the parabolic rate law, regardless of oxygen pressure. The oxidation rate constants of the alloy steadily increased with increasing oxygen pressure. The oxidation mechanism of the MEA was mainly controlled by outward cation diffusion to form an exclusive Cr2O3 layer although minor amounts of Co- or Ni-Cr spinels were observed at PO2 = 10(5) Pa under TEM analyses. The main diffusing species were doubly- and triply-ionized cation vacancies. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/17399 | ISSN: | 0010-938X | DOI: | 10.1016/j.corsci.2021.109411 |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。