標題: | Effects of heat treatments on the microstructure and environment-induced cracking of CF8A steel in simulated BWR water | 作者: | Chen, Tai-Cheng Huang, Jiunn-Yuan Shiue, Ren-Kae Tsay, Leu-Wen |
關鍵字: | CF8A;Heat treatment;Environment-induced cracking;Boiling water reactor | 公開日期: | 1-六月-2021 | 出版社: | ELSEVIER SCI LTD | 卷: | 191 | 來源出版物: | INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING | 摘要: | The effects of heat treatments on the susceptibility to environment-induced cracking (EIC) of the CF8A stainless steel (SS) in simulated water of a boiling water reactor (BWR) were investigated by slow strain-rate tensile (SSRT) tests. Different microstructures were resulted by subjecting the as-casted CF8A to stress relief treatment (1050 degrees C/2 h, C sample), thermal aging (385 degrees C/20000 h, A sample), recovery annealing (500 degrees C/1 h, R sample) or solution annealing (1200 degrees C/2 h, S sample). The results indicated that after aging treatment (A sample), a decrease in tensile ductility and impact toughness was resulted relative to the un-aged specimens. Recovery annealing (R sample) caused an improved tensile ductility and impact toughness of the embrittled CF8A. Excessive solution (S sample) led to an obvious decrease in tensile strength but increase in ductility and toughness of the CF8A. The EIC susceptibility of the tested samples in simulated BWR water increased in the order: S < C < R < A samples. The cracks in distinct CF8A specimens were found to initiate at and propagate along delta/gamma interfaces in simulated BWR water. The lowered ferrite content and change in ferrite morphology accounted for the superior EIC resistance of the S sample relative to that of the other ones in simulated BWR water. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/17401 | ISSN: | 0308-0161 | DOI: | 10.1016/j.ijpvp.2021.104382 |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。