http://scholars.ntou.edu.tw/handle/123456789/24579
標題: | Mitigating Stress Corrosion Cracking of 304L and 316L Laser Welds in a Salt Spray through Micro-Shot Peening | 作者: | Kang, Chia-Ying Chen, Tai-Cheng Shiue, Ren-Kae Tsay, Leu-Wen |
關鍵字: | cold rolling;laser weld;micro-shot peening;stress corrosion cracking;pitting corrosion | 公開日期: | 1-十一月-2023 | 出版社: | MDPI | 卷: | 13 | 期: | 11 | 來源出版物: | METALS | 摘要: | Two austenitic stainless steel (ASS) plates, 304L and 316L, were cold-rolled (304R and 316R) with a 10% reduction in thickness and then subjected to laser welding. Cold rolling caused slight surface hardening and introduced residual tensile stress into the ASS plates. The susceptibility to stress corrosion cracking (SCC) of the welds (304RW and 316RW) was determined using the U-bend test pieces in a salt spray. To highlight the stress concentration at the weld's fusion boundary (FB), the top weld reinforcement was not ground off before bending. Moreover, micro-shot peening (MSP) was performed to mitigate the SCC of the welds by imposing high residual compressive stress and forming a fine-grained structure. Cold rolling increased the susceptibility of the 304R specimen to pitting corrosion and intergranular (IG) microcracking. Moreover, pitting corrosion and SCC were found more often at the FBs of the 304RW. The corrosion pits of the peened 304RW (304RWSP) were finer but greater in amount than the those of the un-peened one. The results also indicated that the 316L ASS welds with MSP were resistant to the incidence of pitting corrosion and SCC in a salt spray. The better reliability and longer service life of dry storage canisters could be achieved by using 316L ASS for the construction and application of MSP on it. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/24579 | DOI: | 10.3390/met13111898 |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。