標題: | Air-Oxidation Behavior of a [(Co50Cr15Mo14C15B6)97.5Er2.5]93Fe7 Bulk-Metallic Glass at 873 K to 973 K (600 °C to 700 °C) | 作者: | Wu Kai Yuan-Hao Wu Wei Shen Chen Jia, H. L. Peter K. Liaw Tao Zhang Rong-Tan Huang |
關鍵字: | Co3O4;Amorphous Alloy;Oxidation Kinetic;Backscatter Electron Image;Glassy Alloy | 公開日期: | 六月-2012 | 出版社: | Springer Nature | 卷: | 43A | 期: | 8 | 起(迄)頁: | 2721 - 2728 | 來源出版物: | Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science | 摘要: | The oxidation behavior of a [(Co50Cr15Mo14C15B6)97.5Er2.5]93Fe7 bulk-metallic glass (Co7-BMG) was studied over the temperature range of 873 K to 973 K (600 °C to 700 °C) in dry air. The oxidation kinetics of the Co7-BMG generally followed the parabolic-rate law, as its oxidation rates increased with temperature. The scaling rate of the Co7-BMG was significantly lower than that of pure Co, which indicates a better oxidation resistance for the amorphous alloy. The scales formed on the Co7-BMG consisted mostly of CoMoO4 and Co3O4, as well as minor amounts of CoO, Cr2O3, and uncorroded Co3B. The formation of CoMoO4 and Cr2O3 is responsible for the lower oxidation rates of the glassy alloy with respect to those of pure Co. In addition, the presence of Co3B further indicated that the crystallization of the amorphous substrate during the oxidation was taken place. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/4482 | ISSN: | 1073-5623 | DOI: | 10.1007/s11661-012-1243-0 |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。