標題: | Reduction of hydrogen embrittlement in an ultra-high-strength steel by laser surface annealing | 作者: | Leu-Wen Tsay Yang, T. Y. |
關鍵字: | composite region;laser-annealed zone;fatigue crack growth rates;hydrogen embrittlement | 公開日期: | 四月-2000 | 卷: | 23 | 期: | 4 | 起(迄)頁: | 325-333 | 摘要: | This paper shows that laser beam irradiation improves the resistance to hydrogen embrittlement (HE) in an ultra-high-strength maraging steel. Localized laser irradiation of a peak-aged steel plate resulted in the formation of a soft surface layer called the laser-annealed zone (LAZ). A composite region (CR) was formed when both the top and bottom surfaces of a peak-aged specimen were laser-annealed (LA) to leave an interior layer of untransformed base metal (BM) sandwiched between the two LAZs. Slow strain rate tensile tests showed that LA specimens had lower strength and ductility than the peak-aged specimens when tested in air, but in a H2S solution, the soft LAZs showed less susceptibility to HE than the BM. The fatigue crack growth rates (FCGRs) in the CR were lower than those in the BM regardless of testing environment and stress ratio (R). The retarded crack growth in the CR was attributed to the combination of residual compressive stresses and the soft microstructures in the LAZs. The tensile fracture appearance of LA specimens tested in a H2S solution exhibited intergranular fracture in the BM. Fractographs of the fatigue specimens tested in gaseous hydrogen revealed transgranular fracture in the LAZs and mainly quasi-cleavage fracture in the BM. |
URI: | http://scholars.ntou.edu.tw/handle/123456789/19974 | ISSN: | 8756-758X |
顯示於: | 光電與材料科技學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。